RG 1101 S

هوموپلیمر

RG 1101 S

POLYMER TYPE: Polypropylene Homopolymer Granule

GRADE NAME: RG 1101 S

APPLICATION: BCF/CF, Carpet yarns, POY/DTY, extrusion laminating

PRODUCT FEATURES: Homopolymer with anti-gas fading stabilization and inherent UV stability

PROCESSING METHOD: Extrusion

24.1 - 26
1550
1500
35
8
23
>50
2.5
1.5
154
78
97
85
163
0.91

g/10min

MPa

kJ/m2

˚C

MPa

R Scale

˚C

g/cm3

ASTM D1238/L

ASTM D790

ASTM D638

ISO 179/ 1eA

ASTM D1525

ISO 2039-1

ASTM D785

ASTM D648

ASTM D3417

ASTM D792

MFR (230 ˚C/ 2.16 kg)

Flexural Modulus

Tensile Modulus of Elasticity (1 mm/min)

Tensile Strength at Yield (50 mm/min)

Tensile Elongation at Yield(50 mm/min)

Tensile Strength at Break (50mm/min)

Tensile Elongation at Break (50 mm/min)

Notched Charpy Impact at 23˚C

Notched Charpy Impact at -30˚C

Vicat Softening Point, 10N

Ball indentation hardness

Rockwell Hardness

HDT (0.46 N/mm2 )

Melting Point, DSC

Density

POLYMER TYPE: "The information in this publication is submitted without prejudice, and is based on our current knowledge and experience and on a limited number of tests. In view of the many factors that may affect processing and application, these data do not relieve the receiver of this information from the responsibility of carrying out their own tests and experiments; neither do they imply and legally binding assurance of certain properties or of suitability for a specific purpose of the products made with or on the basis of the information in this publication." Regal Petrochemical & Industrial Complex